How to choose the diamond saw blade head?

1. Selection of diamond particle size

When the diamond particle size is coarse and single particle size, the saw blade head is sharp and the sawing efficiency is reduced, but the bending strength of the diamond agglomeration decreases; when the diamond particle size is fine or the coarse and fine particle size is mixed, the saw blade head is durable, but the efficiency is lower. Low. Considering the above factors, it is more appropriate to choose the diamond particle size as 50/60 mesh.

2. Selection of diamond distribution concentration

Within a certain range, when the diamond concentration changes from low to low, the sharpness and sawing efficiency of the saw blade gradually decline, while the service life gradually extends; but if the concentration is too high, the saw blade will become dull. However, with low concentration and coarse particle size, the efficiency will be improved. Taking advantage of the different functions of each part of the cutter head during sawing, different concentrations are used (that is, a lower concentration can be used for the middle layer in a three-layer or multi-layer structure). It is beneficial to prevent the saw blade from swaying, thereby improving the quality of stone processing.

3. The choice of diamond strength

The strength of diamond is an important indicator to ensure cutting performance. Excessive strength will make the crystal not easy to be broken, the abrasive grains will be polished during use, and the sharpness will decrease, resulting in the deterioration of tool performance; when the diamond strength is not enough, it will be easily broken after being impacted, and it is difficult to bear the heavy responsibility of cutting. Therefore, the strength should be selected between 130 and 140N.

4. Selection of binder phase

The performance of the saw blade depends not only on the diamond, but on the overall performance of the composite material of the cutter head formed by the proper combination of diamond and binder. For soft stones such as marble, the mechanical properties of the cutter head are required to be relatively low, and copper-based binders can be used. However, the copper-based binder has low sintering temperature, low strength and hardness, high toughness, and low bonding strength with diamond. When adding tungsten carbide (WC), use WC or W2C as the skeleton metal, with an appropriate amount of cobalt to improve the strength, hardness and bonding characteristics, and add a small amount of metals such as Cu, Sn, Zn, etc. with low melting point and low hardness for bonding Mutually. The particle size of the main additive component should be finer than 200 mesh, and the particle size of the additive component should be finer than 300 mesh.

5. Selection of sintering process

With the increase of temperature, the degree of densification of the matrix increases, and the flexural strength also increases, and with the extension of the holding time, the flexural strength of the blank matrix and diamond agglomerates increases first and then decreases. 120s sintering process at ℃ to meet the performance requirements.